Density
|
0.865 g/cm3
|
|
Fabrication Method
|
Injection Molding
|
|
Functionality
|
Mechanical Performance, Sealant (non-peelable)
|
|
Haze (ASTM D1003)
|
3.2 %
|
|
Melt Index ((g/10min @190°C/2.16 kg) (ASTM D1238))
|
8, 8 ((g/10min @230°C/2.16 kg) (ASTM D1238))
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
55 (131)
|
|
Tensile Elongation at Break, MD
|
600 (ASTM D638) %
|
|
Tensile Elongation at Break, TD
|
600 (ASTM D638) %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
6.8 (986) (ASTM D638)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
6.8 (986) (ASTM D638)
|
|
Vicat Softening Point in °C(°F)
|
< 20 (< 68)
|