Properties

app.properties.Title

Anti-block No
Slip false

typical.properties.Title

Density 0.876 g/cm3
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 590 g
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 1300 g
Fabrication Method Blow Molding, Blown Film Extrusion, Oriented (Machine Direction), Sheet Extrusion
Functionality Mechanical Performance, Sealant (non-peelable)
Haze (ASTM D1003) 5 %
Heat Seal Initiation Temp in °C(°F) 60 (140)
Melt Index ((g/10min @190°C/2.16 kg) (ASTM D1238)) 2
Melting Point, DSC (Dow Method) in °C(°F) 82.2 (180)
Tensile Elongation at Break, MD 690 (ASTM D638) %
Tensile Elongation at Break, TD 690 (ASTM D638) %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 29.5 (4280)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 26.3 (3810)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 10.7 (1550)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 10.1 (1460)
Vicat Softening Point in °C(°F) 63 (145)