Density
|
0.888 g/cm3
|
|
Fabrication Method
|
Blow Molding, Blown Film Extrusion, Oriented (Machine Direction), Sheet Extrusion
|
|
Haze (ASTM D1003)
|
18.1 %
|
|
Melt Index ((g/10min @190°C/2.16 kg) (ASTM D1238))
|
2
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
107 (225)
|
|
Tensile Elongation at Break, MD
|
680 (ASTM D638) %
|
|
Tensile Elongation at Break, TD
|
680 (ASTM D638) %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
26 (3770) (ASTM D638)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
26 (3770) (ASTM D638)
|
|
Vicat Softening Point in °C(°F)
|
94 (201)
|