Properties

Key Properties
Density 0.953 g/cm3
Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238)) 33
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 0.38

Application Benefits
Anti-block No
Slip No

Typical Properties
2% Secant Modulus, MD (ASTM D882) in MPa (psi) 1000 (150000)
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 1000 (150000)
Brittleness Temperature in °C(°F) < -76.1
Density Range .951-.960
ESCR-Environmental Stress Crack Resistance (100% IGEPAL) 50 hr
Fabrication Method Blow Molding
Functionality Mechanical Performance
Impact Strength in MPa (psi) 168 kJ/m2 (80 ft lb/in2) ASTM D1822
Tensile Elongation at Break, MD 1000 %
Tensile Elongation at Break, TD 1000 %
Tensile Strength Break, MD (ASTM D638) in MPa (psi) 31 (4500)
Tensile Strength Break, TD (ASTM D638) in MPa (psi) 31 (4500)
Tensile Strength Yield, MD (ASTM D638) in MPa (psi) 26.9 (3900)
Tensile Strength Yield, TD (ASTM D638) in MPa (psi) 26.9 (3900)