Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
640 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
320 g
|
|
Fabrication Method
|
Blown Film Extrusion
|
|
Gloss (45 degree)
|
79
|
|
Haze (ASTM D1003)
|
3 %
|
|
Tensile Elongation at Break, MD
|
480 %
|
|
Tensile Elongation at Break, TD
|
530 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
23.1 (3350)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
18.7 (2710)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
3.50 (508)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
4.80 (696)
|