2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
181 (26300) (ISO 527-3)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
204 (29600) (ISO 527-3)
|
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
> 850 g (ISO 7765-1/B)
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
780 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
980 g
|
|
Enhanced LLDPE
|
Yes
|
|
Fabrication Method
|
Blown Film Extrusion
|
|
Functionality
|
Mechanical Performance, Sealant (non-peelable)
|
|
Gloss (45 degree)
|
64
|
|
Haze (ASTM D1003)
|
13 %
|
|
Heat Seal Initiation Temp in °C(°F)
|
95°C
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
123 (253)
|
|
Vicat Softening Point in °C(°F)
|
100°C (212°F)
|