2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
133 (19400)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
147 (21400)
|
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
630 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
400 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
520 g
|
|
Enhanced LLDPE
|
No
|
|
Fabrication Method
|
Blown Film Extrusion
|
|
Functionality
|
Mechanical Performance
|
|
Gloss (45 degree)
|
47
|
|
Haze (ASTM D1003)
|
16 %
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
119 (246)
|
|
Vicat Softening Point in °C(°F)
|
102 (216)
|