Properties

app.properties.Title

Anti-block No
Slip No

typical.properties.Title

Density 0.941 g/cm3
Fabrication Method Compression Molding, Pipe Extrusion
Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238)) 0.54
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 0.54
Tensile Elongation at Break, MD 780 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 37.0 (5370)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 20.3 (2940)
Vicat Softening Point in °C(°F) 126 (259)