2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
152 (22000)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
159 (23000)
|
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
800 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
350 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
600 g
|
|
Enhanced LLDPE
|
No
|
|
Fabrication Method
|
Blown Film Extrusion
|
|
Functionality
|
Mechanical Performance
|
|
Gloss (45 degree)
|
30
|
|
Haze (ASTM D1003)
|
23 %
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
122 (252)
|
|
Vicat Softening Point in °C(°F)
|
105 (221)
|