2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
160 (23200)
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
165 (23900)
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
220 g
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
400 g
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
600 g
|
Fabrication Method
|
Blown Film Extrusion
|
Functionality
|
Mechanical Performance
|
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238))
|
1
|
Melting Point, DSC (Dow Method) in °C(°F)
|
119 (246)
|
Vicat Softening Point in °C(°F)
|
102 (216)
|