2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
235 (34100)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
281 (40800)
|
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
220 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
250 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
590 g
|
|
Enhanced LLDPE
|
No
|
|
Fabrication Method
|
Blown Film Extrusion, Compression Molding
|
|
Functionality
|
Mechanical Performance
|
|
Gloss (45 degree)
|
80
|
|
Haze (ASTM D1003)
|
9 %
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
121 (250)
|
|
Vicat Softening Point in °C(°F)
|
112 (234)
|