Properties
Key Properties |
|
|---|---|
| Density | 0.939 g/cm3 |
| Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238)) | 22 |
Application Benefits |
|
|---|---|
| Anti-block | No |
| Slip | No |
Typical Properties |
|
|---|---|
| 2% Secant Modulus, MD (ASTM D882) in MPa (psi) | 500 (72500) |
| ESCR-Environmental Stress Crack Resistance (10% IGEPAL) | >2000 hr - 50˚C (122˚F) |
| Fabrication Method | Pipe Extrusion |
| Tensile Elongation at Break, MD | 700 % |
| Tensile Strength Break, MD (ASTM D882) in MPa (psi) | 26.0 (3770) |
| Tensile Strength Yield, MD (ASTM D882) in MPa (psi) | 20.0 (2900) |
| Vicat Softening Point in °C(°F) | 121 (250) |