Properties

Key Properties
Density 0.923 g/cm3
Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238)) 3.5
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 3.5

Application Benefits
Anti-block Yes
Slip Yes

Typical Properties
2% Secant Modulus, MD (ASTM D882) in MPa (psi) 190 (27600)
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 175 (25400)
Dart Drop Impact (ASTM D1709A) in grams (lbs) 120 g (ISO 7765-1a-/A)
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 500 g
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 400 g
Fabrication Method Blown Film Extrusion
Functionality Optical Performance, Processing
Gloss (45 degree) 70
Haze (ASTM D1003) 7 %
Tensile Elongation at Break, MD 450 %
Tensile Elongation at Break, TD 650 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 17 (2470)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 15 (2180)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 9 (1310)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 9 (1310)
Vicat Softening Point in °C(°F) 93 (199)