app.properties.Title
Anti-block No
Collation Shrink Usage Retail
Slip No
typical.properties.Title
2% Secant Modulus, MD (ASTM D882) in MPa (psi) 215 (31200)
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 222 (32200)
Dart Drop Impact (ASTM D1709A) in grams (lbs) 110 g
Density 0.928 g/cm3
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 200 g
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 240 g
Fabrication Method Blown Film Extrusion
Functionality Optical Performance, Processing
Gloss (45 degree) 64
Haze (ASTM D1003) 8.5 %
Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238)) 0.9
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 0.9
Tensile Elongation at Break, MD 380 %
Tensile Elongation at Break, TD 510 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 21 (3050)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 18 (2610)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 12 (1740)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 13 (1890)
Vicat Softening Point in °C(°F) 104 (219)