2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
159 (23100)
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
163 (23600)
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
140 g
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
240 g
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
260 g
|
Fabrication Method
|
Blown Film Extrusion
|
Functionality
|
Mechanical Performance, Optical Performance
|
Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238))
|
0.75
|
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238))
|
0.8
|
Tensile Elongation at Break, MD
|
390 %
|
Tensile Elongation at Break, TD
|
520 %
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
20 (2900)
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
18 (2610)
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
11 (1600)
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
11 (1600)
|
Vicat Softening Point in °C(°F)
|
99 (210)
|