Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
190 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
290 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
250 g
|
|
Fabrication Method
|
Blown Film Extrusion, Blown Film Extrusion
|
|
Functionality
|
Optical Performance, Processing
|
|
Gloss (45 degree)
|
55
|
|
Haze (ASTM D1003)
|
9 %
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
4 J/cm3 (48.3 ft lb/in3)
|
|
Tensile Elongation at Break, MD
|
520 %
|
|
Tensile Elongation at Break, TD
|
850 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
21 (3050)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
23 (3340)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
11 (1600)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
10 (1450)
|