2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
1000 (145000)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
1000 (145000)
|
|
Brittleness Temperature in °C(°F)
|
-75
|
|
Density Range
|
.951-.960
|
|
Fabrication Method
|
Injection Molding
|
|
Functionality
|
Mechanical Performance
|
|
Impact Strength in MPa (psi)
|
63 kJ/m2 (30 ft lb/in2) ASTM D1822
|
|
Structure Type
|
Monolayer, Multilayer
|
|
Tensile Elongation at Break, MD
|
10 %
|
|
Tensile Elongation at Break, TD
|
10 %
|
|
Tensile Strength Break, MD (ASTM D638) in MPa (psi)
|
28.3 (4100)
|
|
Tensile Strength Break, TD (ASTM D638) in MPa (psi)
|
28.3 (4100)
|
|
Tensile Strength Yield, MD (ASTM D638) in MPa (psi)
|
17.2 (2500) )
|
|
Tensile Strength Yield, TD (ASTM D638) in MPa (psi)
|
17.2 (2500) )
|