2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
317 (46000) (ASTM D790)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
317 (46000) (ASTM D790)
|
|
Fabrication Method
|
Injection Molding
|
|
Functionality
|
Mechanical Performance
|
|
Impact Strength in MPa (psi)
|
252 kJ/m2 (120 ft lb/in2) ASTM D1822
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
110 (230)
|
|
Tensile Elongation at Break, MD
|
40 (ASTM D638) %
|
|
Tensile Elongation at Break, TD
|
40 (ASTM D638) %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
11.7 (1700) (ASTM D638)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
10.3 (1500) (ASTM D638)
|