Properties

app.properties.Title

Anti-block No
Slip No

typical.properties.Title

Dart Drop Impact (ASTM D1709A) in grams (lbs) 88 g
Density 0.921 g/cm3
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 440 g
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 480 g
Fabrication Method Blown Film Extrusion, Cast Film Extrusion
Functionality Optical Performance, Processing
Gloss (45 degree) 76
Haze (ASTM D1003) 6.7 %
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 1.9
Melting Point, DSC (Dow Method) in °C(°F) 111 (232)
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3) 4.22 J/cm3 (2210 ft lb/in3)
Tensile Elongation at Break, MD 650 %
Tensile Elongation at Break, TD 730 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 25.5 (3700)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 19.6 (2840)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 12.2 (1760)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 11.8 (1710)
Vicat Softening Point in °C(°F) 92.2 (198)