2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
966 (140000)
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
1100 (159000)
|
Fabrication Method
|
Blown Film Extrusion
|
Functionality
|
Mechanical Performance
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
10.6 (128)
|
Tensile Elongation at Break, MD
|
330 %
|
Tensile Elongation at Break, TD
|
410 %
|
Tensile Strength Break, MD (ASTM D638) in MPa (psi)
|
93.4 (13600) ASTM D882
|
Tensile Strength Break, TD (ASTM D638) in MPa (psi)
|
68.8 (9990) ASTM D882
|
Tensile Strength Yield, MD (ASTM D638) in MPa (psi)
|
42.4 (6140) ASTM D882
|
Tensile Strength Yield, TD (ASTM D638) in MPa (psi)
|
31.8 (4610) ASTM D882
|