CONTINUUM™ DMDC-1270 NT 7 Bimodal Polyethylene Resins
High density polyethylene resin with excellent stiffness, impact strength, and stress crack resistance used in compression and injection molded closure applications such as carbonated soft drinks.
Properties
These values are typical properties and are not intended for use in preparing specifications.
- 2% Secant Modulus, MD (ASTM D882) in MPa (psi) Yes No 1030 (150000)
- 2% Secant Modulus, TD (ASTM D882) in MPa (psi) Yes No 1030 (150000)
- Anti-block Yes No false
- Density (ASTM D792) Yes No 0.955 g/cm3
- ESCR-Environmental Stress Crack Resistance (10% IGEPAL) Yes No 100 hr
- ESCR-Environmental Stress Crack Resistance (100% IGEPAL) Yes No > 1000 hr
- Melt Index (g/10min @190°C/21.6 kg) Yes No 2.5 g/10minutes
- Slip Yes No true
- Tensile Elongation at Break, MD Yes No 920 %
- Tensile Elongation at Break, TD Yes No 920 %
- Tensile Strength Break, MD (ASTM D638) in MPa (psi) Yes No 26 (3770)
- Tensile Strength Break, TD (ASTM D638) in MPa (psi) Yes No 26 (3770)
- Tensile Strength Yield, MD (ASTM D638) in MPa (psi) Yes No 27 (3920)
- Tensile Strength Yield, TD (ASTM D638) in MPa (psi) Yes No 27 (3920)