2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
149 (21600)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
147 (21300)
|
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
66
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
37
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
370
|
|
Enhanced LLDPE
|
No
|
|
Fabrication Method
|
Cast Film Extrusion
|
|
Functionality
|
Mechanical Performance
|
|
Haze (ASTM D1003)
|
.560 %
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
116 (241)
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
9.02 (109)
|
|
Tensile Elongation at Break, MD
|
450 %
|
|
Tensile Elongation at Break, TD
|
680 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
39.6 (5740)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
20.6 (2990)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
10.7 (1550)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
8.96 (1300)
|
|
Vicat Softening Point in °C(°F)
|
96.1 (205)
|