2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
181 (26200)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
212 (30800)
|
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
55 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
260 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
120 g
|
|
Fabrication Method
|
Blown Film Extrusion
|
|
Functionality
|
Optical Performance, Processing
|
|
Gloss (45 degree)
|
60
|
|
Haze (ASTM D1003)
|
8 %
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
109 (228)
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
2.48 J/cm3 (30 ft lb/in3)
|
|
Tensile Elongation at Break, MD
|
150 %
|
|
Tensile Elongation at Break, TD
|
380 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
23.1 (3350)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
13.4 (1950)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
10.7 (1550)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
11.7 (1700)
|
|
Vicat Softening Point in °C(°F)
|
91 (196)
|