Density
|
0.905 g/cm3
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
200 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
360 g
|
|
Fabrication Method
|
Sheet Extrusion
|
|
Functionality
|
Mechanical Performance, Sealant (non-peelable)
|
|
Haze (ASTM D1003)
|
4 %
|
|
Melt Index ((g/10min @190°C/2.16 kg) (ASTM D1238))
|
0.8, 0.80
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
101 (214)
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
29 (350 )
|
|
Tensile Elongation at Break, MD
|
390 %
|
|
Tensile Elongation at Break, TD
|
500 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
44.8 (6500)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
37.9 (5500)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
5.86 (850)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
5.52 (800)
|
|
Vicat Softening Point in °C(°F)
|
95 (203)
|