Density
|
0.91 g/cm3, 0.910 g/cm3
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
180 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
360 g
|
|
Fabrication Method
|
Cast Film Extrusion
|
|
Functionality
|
Sealant (non-peelable)
|
|
Haze (ASTM D1003)
|
0.7 %
|
|
Heat Seal Initiation Temp in °C(°F)
|
99 (210)
|
|
Melt Index ((g/10min @190°C/2.16 kg) (ASTM D1238))
|
3.5
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
103 (217)
|
|
Tensile Elongation at Break, MD
|
530 %
|
|
Tensile Elongation at Break, TD
|
670 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
45 (6530)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
33 (4790)
|
|
Vicat Softening Point in °C(°F)
|
95 (203)
|