Properties
Performance Ratings |
|
|---|---|
| Alkyd Adhesion | Best |
| Block Resistance | Best |
| Chalk Adhesion | Good |
| Cracking Resistance | Good |
| Dirt Pick-Up Resistance | Better |
| Efflorescence Resistance | Good |
| Flaking Resistance | Good |
| Gloss Capability | Best |
| Gloss Potential | Better |
| Gloss Retention | Better |
| Light Duty Corrosion Resistance | Better |
| Print Resistance | Better |
| Stain Blocking | Better |
| Stain Removal | Best |
| Stain Resistance | Best |
| Tint Retention | Good |
| TiO2 efficiency | Better |
Application Benefits |
|
|---|---|
| Performance Benefits | Gloss Potential, Hardness Development, Tear Strength, Tensile Strength, TiO2 Efficiency |
| Resistance | Block, Chemical, Oil Softening, Stain |
Product Use and Formulating |
|
|---|---|
| Type | 1 part |
Sustainability & Safety |
|
|---|---|
| Emissions Standards | Low VOC Capable |
| Ingredient Information | Made without APEO, Styrene Free |
| VOC Capable | < 50 g/liter |
Typical Properties |
|
|---|---|
| Adhesion | Alkyd, Drywall / Wallboard, Previously Painted, Wood, Wood Composite |
| Chemistry | 100% Acrylic |
| Crosslinking Chemistry | Self Crosslinking |
| Functionality | Crosslinkable |
| Ionic Nature | Anionic |
| MFFT-Minimum Film Formation Temp | < 5 °C |
| pH | 8.9 |
| Solids, by weight, % | 45 % |
| System | Water-based |
| Tg-Glass Transition Temp | 5 °C |
| Viscosity (Brookfield LVT #2, 60rpm), cps | 500 cP |