2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
123 (17800)
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
124 (18000)
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
1700 g
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
240 g
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
460 g
|
Enhanced LLDPE
|
Yes
|
Fabrication Method
|
Blown Film Extrusion
|
Functionality
|
Mechanical Performance, Sealant (peelable)
|
Gloss (45 degree)
|
42
|
Haze (ASTM D1003)
|
12 %
|
Melting Point, DSC (Dow Method) in °C(°F)
|
108 (226)
|