Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
110 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
430 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
370 g
|
|
Fabrication Method
|
Blown Film Extrusion, Cast Film Extrusion
|
|
Functionality
|
Optical Performance, Processing
|
|
Gloss (45 degree)
|
66
|
|
Haze (ASTM D1003)
|
7.5 %
|
|
Tensile Elongation at Break, MD
|
400 %
|
|
Tensile Elongation at Break, TD
|
550 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
20.9 (3030)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
18.1 (2630)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
10.3 (1490)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
12.2 (1770)
|
|
Vicat Softening Point in °C(°F)
|
99 (210)
|