Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
88 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
440 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
480 g
|
|
Fabrication Method
|
Blown Film Extrusion, Cast Film Extrusion
|
|
Functionality
|
Optical Performance, Processing
|
|
Gloss (45 degree)
|
76
|
|
Haze (ASTM D1003)
|
6.7 %
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
111 (232)
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
4.22 J/cm3 (2210 ft lb/in3)
|
|
Tensile Elongation at Break, MD
|
650 %
|
|
Tensile Elongation at Break, TD
|
730 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
25.5 (3700)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
19.6 (2840)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
12.2 (1760)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
11.8 (1710)
|
|
Vicat Softening Point in °C(°F)
|
92.2 (198)
|