Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
250 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
300 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
200 g
|
|
Fabrication Method
|
Blown Film Extrusion, Blown Film Extrusion
|
|
Functionality
|
Optical Performance, Processing
|
|
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238))
|
0.25
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
111 (232)
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
3.64 J/cm3 (44 ft lb/in3)
|
|
Tensile Elongation at Break, MD
|
330 %
|
|
Tensile Elongation at Break, TD
|
620 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
24.8 (2600)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
26.4 (3820)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
13.3 (1930)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
11.6 (1690)
|
|
Vicat Softening Point in °C(°F)
|
95 (203)
|