Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
190 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
300 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
180 g
|
|
Fabrication Method
|
Blown Film Extrusion, Blown Film Extrusion
|
|
Functionality
|
Processing
|
|
Gloss (45 degree)
|
50
|
|
Haze (ASTM D1003)
|
11.3 %
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
110 (230)
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
5.71 J/cm3 (69 ft lb/in3)
|
|
Tensile Elongation at Break, MD
|
470 %
|
|
Tensile Elongation at Break, TD
|
660 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
31.8 (4610)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
28.9 (4190)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
12.1 (1750)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
12.1 (1750)
|
|
Vicat Softening Point in °C(°F)
|
96.1 (205)
|