Bottles and Drums Use
|
Food
|
|
Density
|
0.902 g/cm3
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
120 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
410 g
|
|
Fabrication Method
|
Blown Film Extrusion, Cast Film Extrusion
|
|
Functionality
|
Sealant (non-peelable)
|
|
Haze (ASTM D1003)
|
0.7 %
|
|
Heat Seal Initiation Temp in °C(°F)
|
93.9 (201)
|
|
Melt Index ((g/10min @190°C/2.16 kg) (ASTM D1238))
|
3
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
98 (208)
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
31.4 (380 )
|
|
Structure Type
|
Multilayer
|
|
Tensile Elongation at Break, MD
|
350 %
|
|
Tensile Elongation at Break, TD
|
570 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
44.6 (6470)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
29.8 (4320)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
9.93 (1440)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
5.45 (790)
|
|
Vicat Softening Point in °C(°F)
|
85 (185)
|