物性
app.properties.Title |
|
|---|---|
| Anti-block | No |
| Slip | false |
typical.properties.Title |
|
|---|---|
| Density | .888 g/cm3 |
| Fabrication Method | Blow Molding, Blown Film Extrusion, Oriented (Machine Direction), Sheet Extrusion |
| Haze (ASTM D1003) | 18.1 % |
| Melt Index ((g/10min @190°C/2.16 kg) (ASTM D1238)) | 2 |
| Melting Point, DSC (Dow Method) in °C(°F) | 107 (225) |
| Tensile Elongation at Break, MD | 680 (ASTM D638) % |
| Tensile Elongation at Break, TD | 680 (ASTM D638) % |
| Tensile Strength Break, MD (ASTM D882) in MPa (psi) | 26 (3770) (ASTM D638) |
| Tensile Strength Break, TD (ASTM D882) in MPa (psi) | 26 (3770) (ASTM D638) |
| Vicat Softening Point in °C(°F) | 94 (201) |