2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
814 (118000)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
814 (118000)
|
|
Bottles and Drums Use
|
Food, Household Industrial Chemicals (HIC) / Agriculture Bottles, Personal Care, Water / Juice / Dairy
|
|
Brittleness Temperature in °C(°F)
|
< -76.1
|
|
ESCR-Environmental Stress Crack Resistance (100% IGEPAL)
|
400 hr
|
|
Fabrication Method
|
Blow Molding
|
|
Functionality
|
Mechanical Performance
|
|
Impact Strength in MPa (psi)
|
147 kJ/m2 (70 ft lb/in2) ASTM D1822
|
|
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238))
|
0.4
|
|
Tensile Elongation at Break, MD
|
770 %
|
|
Tensile Elongation at Break, TD
|
770 %
|
|
Tensile Strength Break, MD (ASTM D638) in MPa (psi)
|
16.5 (2400)
|
|
Tensile Strength Break, TD (ASTM D638) in MPa (psi)
|
16.5 (2400)
|
|
Tensile Strength Yield, MD (ASTM D638) in MPa (psi)
|
23.8 (3450)
|
|
Tensile Strength Yield, TD (ASTM D638) in MPa (psi)
|
23.8 (3450)
|