物性

主要特性

Density 0.949 g/cm3
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 0.25

アプリケーションの利点

Anti-block No
Slip No

代表的な物性

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 900 (130000)
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 900 (130000)
Bottles and Drums Use Food, Household Industrial Chemicals (HIC) / Agriculture Bottles, Personal Care, Water / Juice / Dairy
Brittleness Temperature in °C(°F) < -76.1
Density Range .940-.950
ESCR-Environmental Stress Crack Resistance (100% IGEPAL) 180 hr
Fabrication Method Blow Molding
Functionality Mechanical Performance
Impact Strength in MPa (psi) 210 kJ/m2 (100 ft lb/in2) ASTM D1822
Tensile Elongation at Break, MD 900 %
Tensile Elongation at Break, TD 900 %
Tensile Strength Break, MD (ASTM D638) in MPa (psi) 31 (4500)
Tensile Strength Break, TD (ASTM D638) in MPa (psi) 31 (4500)
Tensile Strength Yield, MD (ASTM D638) in MPa (psi) 23.4 (3400)
Tensile Strength Yield, TD (ASTM D638) in MPa (psi) 23.4 (3400)