2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
2 mil - 138 (20000)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
2 mil - 138 (19900)
|
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
.8 mil - 130 g (ASTM D1709A), .8 mil - < 100 g (ASTM D1709B)2, 2 mil - 210 (ASTM D1709B), 2 mil - 330 (ASTM D1709A)
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
2 mil - 790 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
2 mil - 1100 g
|
|
Enhanced LLDPE
|
No
|
|
Fabrication Method
|
Sheet Extrusion
|
|
Functionality
|
Mechanical Performance
|
|
Gloss (45 degree)
|
95
|
|
Haze (ASTM D1003)
|
1 %
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
123 (253)
|
|
Vicat Softening Point in °C(°F)
|
98.9 (210)
|