物性

未硬化特性

Appearance Black

硬化後特性

Density 1.17 g/cm3
Durometer/Hardness, JIS Type A 63
Tear Strength Die-Angle 15 N/mm
Tensile Elongation 240 %
Tensile Strength 5.6 MPa

硬化条件

Curing Agent SILASTIC™ RC-3 40P Rubber Additive, 4.5 parts
Curing Condition, Molded 10min/150 °C
Curing Condition, Post-cured 4hours/200 °C