物性

未硬化特性

Appearance White
Plasticity 253 mm/100

硬化後特性

Density 1.25 g/cm3
Durometer/Hardness, JIS Type A 66
Tear Strength Die-Angle 23 N/mm
Tear Strength Die-Crescent 7 N/mm
Tensile Elongation 270 %
Tensile Strength 10.1 MPa

硬化条件

Curing Agent SILASTIC™ RC-14 A Rubber Additive, 1.3 parts
Curing Condition, Molded 10min/120 °C
Curing Condition, Post-cured 1hours/150 °C