物性
主要特性 |
|
|---|---|
| Density | 0.95 g/cm3, 0.950 g/cm3 |
| Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238)) | 7 |
| Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) | 0.1, 0.10 |
アプリケーションの利点 |
|
|---|---|
| Anti-block | No |
| Slip | No |
代表的な物性 |
|
|---|---|
| Brittleness Temperature in °C(°F) | < -75 |
| Density Range | .951-.960 |
| Fabrication Method | Pipe Extrusion, Profile Extrusion |
| Tensile Elongation at Break, MD | > 500 % |
| Tensile Elongation at Break, TD | > 500 % |
| Tensile Strength Yield, MD (ASTM D638) in MPa (psi) | >24.1 (> 3500) |
| Tensile Strength Yield, TD (ASTM D638) in MPa (psi) | >24.1 (> 3500) |