物性

主要特性

Density 0.965 g/cm3
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 2.7

アプリケーションの利点

Anti-block No
Closure Type Caps, Hot Fill / Aseptic
Slip No

代表的な物性

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 1410 (204000)
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 1410 (204000)
Density Range .961+
ESCR-Environmental Stress Crack Resistance (10% IGEPAL) 28 hr
ESCR-Environmental Stress Crack Resistance (100% IGEPAL) 35 hr
Fabrication Method Compression Molding, Injection Molding
Functionality Mechanical Performance
Tensile Elongation at Break, MD 700 %
Tensile Elongation at Break, TD 700 %
Tensile Strength Break, MD (ASTM D638) in MPa (psi) 20.7 (3000)
Tensile Strength Break, TD (ASTM D638) in MPa (psi) 20.7 (3000)
Tensile Strength Yield, MD (ASTM D638) in MPa (psi) 29.6 (4300)
Tensile Strength Yield, TD (ASTM D638) in MPa (psi) 29.6 (4300)