物性

主要特性

Density 0.902 g/cm3
Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238)) 0.85 (g/10min @190°C/2.16 kg) (ASTM D1238)
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 0.85

代表的な物性

Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 640 g
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 320 g
Fabrication Method Blown Film Extrusion
Gloss (45 degree) 79
Haze (ASTM D1003) 3 %
Tensile Elongation at Break, MD 480 %
Tensile Elongation at Break, TD 530 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 23.1 (3350)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 18.7 (2710)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 3.50 (508)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 4.80 (696)