物性
主要特性 |
|
|---|---|
| Density | 0.919 g/cm3 |
| Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) | 1.1 |
アプリケーションの利点 |
|
|---|---|
| Anti-block | No |
| Slip | No |
代表的な物性 |
|
|---|---|
| 2% Secant Modulus, MD (ASTM D882) in MPa (psi) | 198 (28700) (ISO 527-3) |
| 2% Secant Modulus, TD (ASTM D882) in MPa (psi) | 238 (34500) (ISO 527-3) |
| Dart Drop Impact (ASTM D1709A) in grams (lbs) | 450 g (ISO 7765-1/A) |
| Enhanced LLDPE | No |
| Fabrication Method | Blown Film Extrusion, Blown Film Extrusion |
| Functionality | Mechanical Performance |
| Gloss (45 degree) | 61 |
| Haze (ASTM D1003) | 8.9 % |
| Vicat Softening Point in °C(°F) | 104 (219) |