2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
327 (47400)
|
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
52
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
43
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
84
|
|
Fabrication Method
|
Cast Film Extrusion
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
0.485 (5.87)
|
|
Tensile Elongation at Break, MD
|
260 %
|
|
Tensile Elongation at Break, TD
|
85 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
12 (1740)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
10.3 (1490)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
15.1 (2190)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
15.1 (2190)
|