物性
主要特性 |
|
---|---|
Density | 0.940 g/cm3 |
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) | 1 |
アプリケーションの利点 |
|
---|---|
Anti-block | No |
Collation Shrink Usage | Logistics, Retail |
Slip | No |
製品の使用と処方 |
|
---|---|
Type | Breathable Blown Film |
代表的な物性 |
|
---|---|
2% Secant Modulus, MD (ASTM D882) in MPa (psi) | 370 (53700) (ISO 527-3) |
2% Secant Modulus, TD (ASTM D882) in MPa (psi) | 420 (60900) (ISO 527-3) |
Dart Drop Impact (ASTM D1709A) in grams (lbs) | 120 g (ISO 7765-1/A) |
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) | 130 g |
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) | 240 g |
Enhanced LLDPE | No |
Fabrication Method | Blown Film Extrusion |
Functionality | Mechanical Performance |
Vicat Softening Point in °C(°F) | 125 (257) |