物性

app.properties.Title

Anti-block No
Slip No

typical.properties.Title

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 578 (83800)
Density 0.939 g/cm3
ESCR-Environmental Stress Crack Resistance (100% IGEPAL) >2000 hr - 100˚C (212˚F)
Fabrication Method Blown Film Extrusion
Functionality Mechanical Performance
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 15.5
Tensile Elongation at Break, MD 630 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 29.0 (4210)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 18.0 (2610)