物性

主要特性

Density 0.923 g/cm3
Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238)) 2
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 2, 2

アプリケーションの利点

Anti-block No
Slip No
Tie Layers No

製品の使用と処方

Type Breathable Blown Film, Breathable Cast Film

代表的な物性

Dart Drop Impact (ASTM D1709A) in grams (lbs) 110 g
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 430 g
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 370 g
Fabrication Method Blown Film Extrusion, Cast Film Extrusion
Functionality Optical Performance, Processing
Gloss (45 degree) 66
Haze (ASTM D1003) 7.5 %
Tensile Elongation at Break, MD 400 %
Tensile Elongation at Break, TD 550 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 20.9 (3030)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 18.1 (2630)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 10.3 (1490)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 12.2 (1770)
Vicat Softening Point in °C(°F) 99 (210)