物性

app.properties.Title

Anti-block Yes
Slip Yes

typical.properties.Title

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 175 (25400)
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 185 (26800)
Dart Drop Impact (ASTM D1709A) in grams (lbs) 170 g
Density 0.924 g/cm3
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 350 g
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 260 g
Fabrication Method Blown Film Extrusion
Functionality Mechanical Performance, Optical Performance
Gloss (45 degree) 58
Haze (ASTM D1003) 9.2 %
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 0.75
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3) 4 J/cm3 (48.3 ft lb/in3)
Tensile Elongation at Break, MD 380 %
Tensile Elongation at Break, TD 570 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 25 (3630)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 23 (3340)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 11 (1600)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 11 (1600)