物性

主要特性

Density 0.922 g/cm3
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 0.3

アプリケーションの利点

Anti-block No
Collation Shrink Usage Logistics, Retail
Slip No
Tie Layers No

代表的な物性

Dart Drop Impact (ASTM D1709A) in grams (lbs) 700 g
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 900 g
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 1400 g
Fabrication Method Blown Film Extrusion
Functionality Mechanical Performance, Optical Performance
Tensile Elongation at Break, MD 580 %
Tensile Elongation at Break, TD 720 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 23 (3340)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 24 (3480)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 10 (1450)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 11 (1600)