物性

主要特性

Density 0.952 g/cm3
Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238)) 5.5

アプリケーションの利点

Anti-block No
Slip No

代表的な物性

Density Range .951-.960
ESCR-Environmental Stress Crack Resistance (100% IGEPAL) > 2000 hr
Fabrication Method Blow Molding
Functionality Mechanical Performance
Melt Index (g/10min @190°C/5.0 kg (ASTM D1238)) 0.19
Tensile Elongation at Break, MD 660 %
Tensile Elongation at Break, TD 660 %
Tensile Strength Break, MD (ASTM D638) in MPa (psi) 32.4 (4700)
Tensile Strength Break, TD (ASTM D638) in MPa (psi) 32.4 (4700)
Tensile Strength Yield, MD (ASTM D638) in MPa (psi) 20.6 (2990)
Tensile Strength Yield, TD (ASTM D638) in MPa (psi) 20.6 (2990)