物性
主要特性 |
|
|---|---|
| Density | 0.935 g/cm3 |
| Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238)) | 7 |
| Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) | 7 |
アプリケーションの利点 |
|
|---|---|
| Anti-block | No |
| Slip | No |
代表的な物性 |
|
|---|---|
| ESCR-Environmental Stress Crack Resistance (10% IGEPAL) | >417 hr - 50˚C (122˚F) |
| ESCR-Environmental Stress Crack Resistance (100% IGEPAL) | >1000 hr - 50˚C (122˚F) |
| Fabrication Method | Injection Molding, Rotational Molding |
| Impact Strength in MPa (psi) | 228J (168ft-lb) - -40˚C (-40˚F, 72J (53ft-lb) - -40˚C (-40˚F |
| Tensile Strength Yield, MD (ASTM D882) in MPa (psi) | 18.4 (2670) |